Slide Plate Copper Powder Sintered, Thickness10mm:TWX,TWXT0 pages
SLIDE PLATE
Oilless Slide Plate Copper Powder Sintered Type Thickness 10mm
SO#220
RoHS
h11
3
10a0.01
1.6
1.6
L2
h17.5
h11
o0.1
W o0.3
R2
W2
R
2
h6.6
R1
tWM28N75
W1
L1a0.2
2.5
10a0.01
6.3
L o0.1
o0.3
or more
6.3
tWM100
o
R
2
W1a0.2
h11
L1a0.2
2.5
10a0.01
L o0.1
o0.3
R
50
25
6.3
h17.5
o0.1
W o0.3
h11 2
LM250
t WM75, LM250Y300
1.6
ttWM48,
L2
L
10a0.01
o0.1
o0.3
TWXT(Sintered, 2-Hole Type)
75
50
37.5
6.3
2
)
h17.5
ll a
.5 (
A
L
C1
rou 2
nd
)
ll a
.5 (
A
t Special
C1
.5 (
A
0
h16 o0.5
(9.4)
ll a
rou 2
nd
)
C1
6
8
0
6.5o0.3
18
20
Materialt
t
t
t
Accessoryt
TWX
18
25
15
28
25
15
38
25
15
TWX
25
48
50
25
15
45
50
100
25
50
75
100
150
100
100
50
75
100
150
58
25
75
50
25
100
50
75
100
150
TWX
TWXT
25
125
50
100
150
200
150
25
Catalog No.
W
o
75
100
125
150
75
100
125
150
75
100
125
150
75
100
125
150
200
250
75
100
150
75
100
125
150
200
250
300
100
125
150
200
250
300
125
150
200
250
300
150
200
250
TWXT
o
100
125
150
200
250
o
125
150
200
250
o
150
200
250
L
TWX
28
o
125
qOperation Range
No lubrication
M10p1.5
(Chamfered shape at both ends)
Order
Lubricating
Condition
brazier head bolt (LCS standard)
0
111
2.5
10a0.01
o0.1
o0.3
LCS-10-20
R1
UWM75 or more
L1a0.2
3.5
R5
UWM38Y48
1.6
rou
nd
2
L2
25
W
Bolts do not accompany with TWX18.
qWe are ready to accept requests or orders for special parts.
W1 and W2 are the dimensions only for TWX (W=100 or more).
R
UWM18Y28
100
Catalog No.
L
15
200
R
h11
Direction
o0.1
W o0.3
t Sliding
45
50
75
100
45
50
75
100
45
50
75
100
45
50
75
200
2.5
L1a0.2
L2
100
h17.5
L2
1.6
W2
o0.1
W o0.3
o
L1
Metal Sliding Materials
WM28 or more
WM18
TWX
Regular lubrication(Grease)
Copper powder sintered(SO#220)
Hatched area sintered
Thickness 1.2mm or more
S45C(Base Plate)
Mounting Bolt
Environment
Condition
Atmosphere
Max. Allowable Load P
2
N/mm
Max. Allowable Sliding Speed V
m/min
Max. Allowable PV value
2
N/mm Ym/min
50
30
100
75
60
150
Operation Range Temperature
˚C
o40ni120
qPhysical Properties
Specific Gravity
3
g/cm
Hardness
HRM
Compression Strength
2
N/mm (0.2% proof stress)
Impregnation Ratio
6.2a0.3
70n90
200n250
18 or more
112
"