Sika® Release LG0 pages
Product Data Sheet
Version 02 / 2011
Sika® Release LG
Areas of Application
Product Benefits
Sika Release LG is designed to release all types
epoxy, phenolic, polyester (GRP) or vinyl ester
resins from composite, steel or aluminum moulds
No release of polyurethane resins possible
®
Easy, fast application
High slip, easy release
Durable, provides multiple releases per
application
High heat resistance
Minimal mould build-up
No shaking or mixing required
Description
Basis
Advanced polymeric resin in a non-chlorinated organic solvent blend, clear, low viscosity
Processing Data
Density
Consumption
g/ml
Brushed coats
0.73
ml/m²
10 (per coat)
Flash point
°C
< 21
Heat distortion temperature
°C
200
Packaging
Individual components
Sika ® Release LG
1 litre
Processing
The material, processing and substrate temperature must be from 18 to 25°C.
Mould cleaning and release agent application should be performed in a well ventilated area.
The mould surfaces must be clean, dry, free of dust and grease before release. Laquer and sealer
coatings should be dried resp. cured.
For removing of wax residues we recommend Sika® Mold Cleaner.
Sika® Release LG can be applied at mould temperatures up to 50°C.
Method of application:
1.t Apply Sika® Release LG to clean, dry cotton cloth.
2.t Wipe wet cloth over mould surface covering an area of approximately 0.5m². Vigorous rubbing or polit
t shing is not required.
3.t Repeat steps 1 and 2 on the adjacent area, frequently reapplying the product to the cloth. Ensure a t
t good overlap with the previous area to provide complete coverage.
4.t Repeat until mould is completely coated.
5.t When dry, allow a further 15 minutes between coats for the film to cure.
6.t Repeat steps 1-5 above for a further 3 coats (4 in total).
7.t When dry, allow final film to cure for at least 30 minutes at room temperature before moulding. Allowing t
t a longer cure or heat curing (e.g. 15 min at 60°C) will improve film durability.
8. When release becomes less easy, apply one further coat of Sika® Release LG in the same way as
t
t described above.
Sika ® Release LG 1 / 2
Tooling & Composites
Semipermanent release agent, free of silicones and halogenes
"