Biresin® M600 pages
Product Data Sheet
nnnnVersion 02/2012
nnnnBiresin® M60
nnnnModel paste
nnnnAreas of Applicatio
nnnnProduct Benefits
nnnnWith hardener Biresin® M60 as hand applicable
nnnnepoxy paste for manufacturing of master models
nnnnin car body construction and in model making
nnnnWith hardener Biresin® F4 for casting
nnnnthicknesses up to 30 - 40 mm
nnnnWith hardener Biresin®S10 for correcting work
nnnnor bonding applications with faster setting
nnnnSpecific lightweight paste
nnnnEasily workable
nnnnGood edge stability
nnnnSetting with low shrinkage
nnnnOne resin component with special hardeners for
nnnndifferent applications
nnnnDescription
nnnnBasis
nnnnResin
nnnnHardener
nnnnHardener
nnnnHardener
nnnnFiller
nnnnTwo-component-epoxy-system
nnnnBiresin® M60, epoxy resin, brown, filled, pasty
nnnnBiresin® M60, amine, white, filled, pasty
nnnnBiresin® S10, amine, amber, unfilled, medium viscous
nnnnBiresin® F4, amine, colourless, unfilled, low viscous
nnnnBiresin®Spachtel braun, two-component-polyester-system
nnnnProcessing Data
nnnnMixing ratio Biresin® M60 resin to hardener in parts by weight | Biresin® M60 | Biresin® S10 | Biresin® F4 |
100 : 30 | 100 : 15 | 100 : 12,5 | |
Mixed viscosity, 25°C | pasty | castable | |
Potlife, RT min | 30 | 15 | 20 |
Demoulding time / Setting time (workable) h | 24 | 16-24 | 24 |
Physical Data (approx. values)
nnnnBiresin® M60 resin with hardener | Biresin® M60 | Biresin® S10 | Biresin® F4 |
Density ISO 845 g/cm3 | 0.77 | 0.7 | 0.75 |
Shore hardness ISO 868 | D65 | D 69 | D 78 |
Flexural strength IS0178 MPa | 25 | 32 | 28 |
Tensile strength ISO 527 MPa | 14 | 13 | |
Compressive strength ISO 604 MPa | 35 | 34 | |
Heat distortion temperature IS075B °C | 47 | ||
Linear shrinkage internal % | 0.016 | 0.016 |
Application data Biresin®Spachtel braun | ||
Mixing ratio in parts by weight | 100 : 2 | |
Potlife, RT min | 5 | |
Setting time, RT min | >20 |
®
"