TECHNICAL DATA SHEET
Apollo 1603 is a single component, medium viscosity cyanoacrylate adhesive. It is suitable for
general-purpose bonding, particularly providing excellent strength and speed on all rubber
compounds. Apollo 1603 is certified to ISO 10993-5, 10993-10 and 10993-11 for biocompatibility,
making it suitable for use in medical applications.
Physical Properties - Monomer (Uncured)
Specifications and Approvals
Base Compound
Ethyl
10993-5: -10; -11
Appearance
Clear
Viscosity
1400 +/- 200
Specific Gravity
1.06 g/cc
Flash Point
85°C/ 185°F
Shelf Life
9 mo
Storage Condition
15.5°C/ 60°F
RoHS-Compliant
yes
80%
Physical Properties - Polymer (Cured)
60%
Full Cure Time
cPs
Hot Strength
100%
Clear
Service Temp Range
-55
(%RT strength, tested at temperature)
120%
24 hours
Appearance
10993-5: -10; -11
40%
to
95 °C
( -67
to
20%
203 °F)
0%
-40°C
0°C
Time Until Full Cure
Setting Time
25 - 45
6-8
4-6
Steel
ABS
EPDM
Wood
seconds
seconds
seconds
100°C
130°C
(% of RT strength)
120%
100%
> 60
80%
Performance of Cured Adhesive
N/mm²
Substrate
50°C
60%
PSI
Steel
15.2
to
18.8
2200
to
2730
40%
Rubber*
5.1
to
15.2
735
to
2200
AL
3.1
to
3.5
450
to
510
20%
PC**
22.3
to
24.9
3240
to
3605
PVC**
18.3
to
26.7
2660
to
3875
ABS**
12.0
to
18.3
1740
to
2660
0%
Cure
5 min
Heat Aging
10 min
30 min
60 min
240 min
(aged at temp indicated and tested @ 22°C)
*Rubber figures given are typical. Your results may vary by specific rubber type.
**Tested to ASTM 4501
***n/r = not recommended
Performance Range, by Substrate
0.0
5.0
10.0
15.0
N/mm2
20.0
25.0
30.0
35.0
40.0
ABS
PVC
PC
AL
Rubber
(typical)
100%
90%
80%
70%
60%
50%
40%
30%
20%
10%
0%
60C
80C
100C
0
1000
2000
Hours
Steel
0
1000
2000
3000
PSI
4000
5000
6000
Cyberbond LLC...
630.761.8900...
.