PTFE260 skived0 pages
PTFE260 skived
High T° Bagging film
DESCRIPTION
PTFE260 skived is a technical bagging film recommended for advanced composite and elastomer fabrication.
PTFE260 skived is a high temperature and good elongation release bagging film suitable for high
temperature cure cycles. Skived PTFE films are manufactured from virgin PTFE, which is pressed into billets,
sintered and skived to the appropriate thickness with tight tolerance control.
PTFE260 belongs to the Polytetrafluoroethylene family : it is a release film with all resins and elastomers.
This film has a good elongation and mechanical characteristics.
STORAGE
Keep this film at room temperature and normal hygrometry.
CHARACTERISTICS
Thickness
Weight
25µ
53 g/m²
50µ
106 g/m²
75µ
PTFE
Color
159 g/m²
Grey - Brown
Perforation
Aspect
Length
Standard
width
No
Smooth
Surface
100 m
Max. Serv. Temp.
Packaging
260°C
Roll
1,20 m
Elongation at break
Tensile strength
MD
TD
MD
TD
280 %
280 %
25 MPa
25 MPa