Apollo 29990 pages
Cyberbond
Apollo
2999
TECHNICAL DATA SHEET
Apollo 2999 is a single component, high viscosity gel cyanoacrylate adhesive. It is ideal for
bonding porous materials, or for applications where controlling adhesive flow is critical.
Apollo 2999 offers maximum gap filling and repositioning time. Apollo 2999 has been
certified to ISO 10993-5 for cytotoxicity, making it appropriate for use in medical device
applications.
Physical Properties - Monomer (Uncured)
Specifications and Approvals
Base Compound
Ethyl
10993-5
Appearance
Gel
Viscosity
11000 +/- 1500
Specific Gravity
1.06 g/cc
Flash Point
85°C/ 185°F
Shelf Life
12 mo
Storage Condition
15.5°C/ 60°F
RoHS-Compliant
yes
80%
Physical Properties - Polymer (Cured)
10993-5
60%
Full Cure Time
Hot Strength
100%
Gel
Service Temp Range
-55
to
(%RT strength, tested at temperature)
120%
24 hours
Appearance
cPs
40%
95 °C
( -67
to
20%
203 °F)
0%
-40°C
0°C
Time Until Full Cure
Setting Time
50
18
15
Steel
ABS
EPDM
seconds
seconds
seconds
50°C
100°C
130°C
(% of RT strength)
120%
100%
80%
Performance of Cured Adhesive
N/mm²
Substrate
60%
PSI
2000
to
2730
40%
15.2
630
to
2200
to
13.2
1510
to
1920
20%
22.3
to
24.9
3240
to
3605
PVC**
18.3
to
26.7
2660
to
3875
ABS**
12.0
to
18.3
1740
to
2660
13.8
to
18.8
Rubber*
4.3
to
AL
10.4
PC**
Steel
0%
Cure
5 min
Heat Aging
10 min
30 min
60 min
240 min
(aged at temp indicated and tested @ 22°C)
*Rubber figures given are typical. Your results may vary by specific rubber type.
**Tested to ASTM 4501
***n/r = not recommended
Performance Range, by Substrate
0.0
5.0
10.0
15.0
N/mm2
20.0
25.0
30.0
35.0
40.0
ABS
PVC
PC
AL
Rubber
(typical)
100%
90%
80%
70%
60%
50%
40%
30%
20%
10%
0%
60C
80C
100C
0
1000
2000
Hours
Steel
0
1000
2000
3000
PSI
4000
5000
6000
Cyberbond LLC...