Apollo H70 pages
Cyberbond
Apollo H7
TECHNICAL DATA SHEET
Apollo H-7 a single component, medium to high viscosity cyanoacrylate adhesive. It is
designed to set and adhere rapidly to inactive surfaces such as wood, leather and
fiberglass matting. Apollo H-7 offers viscosity and flow characteristics that are ideal for
filling medium gaps.
Physical Properties - Monomer (Uncured)
Base Compound
Appearance
Specifications and Approvals
0
Ethyl
Clear
None
Viscosity
750 +/- 150
Specific Gravity
1.06 g/cc
Flash Point
85°C/ 185°F
Shelf Life
12 mo
Storage Condition
20°C/ 68°F
RoHS-Compliant
yes
80%
Physical Properties - Polymer (Cured)
60%
Full Cure Time
Hot Strength (%RT strength, tested at temperature)
120%
100%
24 hours
Appearance
cPs
Clear
Service Temp Range
-55
to
40%
95 °C
( -67
to
20%
203 °F)
0%
-40°C
0°C
50°C
100°C
130°C
Time Until Full Cure (% of RT strength)
Setting Time
15
15
10
Steel
ABS
EPDM
seconds
seconds
seconds
120%
100%
80%
Performance of Cured Adhesive
N/mm²
Substrate
60%
PSI
2260
to
2460
40%
15.2
690
to
2200
16.1
2070
2330
20%
to
to
27.8
3375
to
4035
17.7
to
24.4
2570
to
3545
14.5
to
17.5
2110
to
2540
15.6
to
17.0
Rubber*
4.8
to
AL
14.3
to
PC**
23.3
PVC**
ABS**
Steel
0%
Cure
5 min
10 min
30 min
60 min
240 min
Heat Aging (aged at temp indicated and tested @ 22°C)
*Rubber figures given are typical. Your results may vary by specific rubber type.
**Tested to ASTM 4501
***n/r = not recommended
100%
Performance Range, by Substrate
0.0
5.0
10.0
15.0
N/mm2
20.0
25.0
30.0
60C
80%
35.0
40.0
80C
100C
60%
ABS
PVC
40%
PC
20%
AL
0%
Rubber
(typical)
0
1000
2000
Hours
Steel
0
1000
2000
3000
PSI
4000
5000
6000
Cyberbond LLC...