TECHNICAL DATA SHEET
Titan 8242 is a single component anaerobic threadlocking adhesive, which is thixotropic
and develops medium strength. Titan 8242 prevents the loosening of threaded fasteners,
and is suitable for applications where disassembly with hand tools is required for
servicing. Titan 8242 is certified to ANSI/NSF 61 Section 6: Drinking Water System
Components.
Physical Properties - Monomer (Uncured)
Base Compound
Appearance
Viscosity
Specifications and Approvals
Dimethacrylate Ester
Blue liquid
Thixotropic 1,200 + 400 @ 20 RPM
Mil-S-46163A, Type II, Grade N; ANSI/NSF 61 Section 6
Hot Strength (%RT strength, tested at temperature)
(Brookfield Spindle 3 @ 20 rpm, RVT, 25°C)
Gap Fill
Specific Gravity
Flash Point
Shelf Life
Storage Condition
RoHS-Compliant
120%
.007"
1.1
>200°F / 93°C
12 months unopened
20°C / 68°F
yes
100%
80%
60%
Physical Properties - Polymer (Cured)
Appearance
Locking Strength
Service Temp Range
Full Cure Time
Pin/Collar Strength
Blue Solid
Medium
-65 to 300 °F
24 hours
1200
psi
8.3
N/mm2
40%
20%
( -54
to
149 °C)
0%
-40°C
inch-pounds
Newton meters
Breakaway Torque
70.0
to
150.0
7.91
to
16.95
Prevailing Torque
30.0
to
100.0
3.39
to
11.30
Setting Time / Full Cure Time*
10
15
20
20
minutes
minutes
minutes
minutes
/
/
/
/
24
24
24
24
200%
175%
150%
125%
100%
75%
50%
25%
0%
100°C
130°C
60C
80C
100C
Hours
0
hrs
hrs
hrs
hrs
1000
2000
3000
Solvent Resistance
Solvent
Alcohol
Ester (aromatic)
*68°F / 20°C, 65% RH
Example
Resistance
Ethanol, Methanol
+++
Ethylacetate
–––
Ketone (aromatic) Acetone, Benzophenone
Steel
0
5
10
15
Set Time in Min
20
25
++–
Benzyl, Toluol, Xylol
++–
Halogenated
hydrocarbons
Brass
Petrol, Heptanes, Hexane
Aromatic
hydrocarbons
Zinc-Plated
–––
Aliphatic
hydrocarbon
(alkanes)
Stainless
Steel
Cyberbond LLC
888.525.6122
50°C
Heat Aging (aged at temp indicated and tested @ 22°C)
Performance of Cured Adhesive
Steel
Brass
Zinc-Plated
Stainless Steel
0°C
Methylenchloride,
Chloroform,
Chlorobenzol
–––
Weak aqueous
acid
Nitrite, muriatic acid,
sulphuric acid,
phosphoric acid
+ + + (– – – if
concentrated)
Weak aqueous
base
sodium hydroxide
solution, caustic potash
+ + + (– – – if
concentrated)