HIGH TEMPERATURE CERAMICS|Innovacera0 pages
CERAMICS FIRING SETTER
Introductions
Innovacera offers a full range of solutions for supporting parts during sintering in reducing or oxidizing
atmospheres up to 1800ºC.
Innovacera has the industry's broadest range of manufacturing methods - including vacuum forming,
casting, pressing and CNC machining. Mullite, alumina and alumina-zirconia compositions are available for
applications in sintering of technical ceramic, electronic ceramic, and powder metal parts.
Properties
Excellent permeability
Excellent binder removability
Strong against thermal shook
Low heat capacity
No warping
Available in various sizes and shapes
Lightweight and easy handling
Technical Ceramics
For firing of heavy loads pressed mullite and mullite-alumina plates have excellent resistance to
sagging. Engineered compositions make smooth and flat surfaces possible while maintaining
excellent thermal shock properties.
For small parts firing, Innovacera offers machinable, low mass alumina fiber based compositions that
eliminate the need for costly hard tooling. This allows manufacturers to customize setter
configuration without costly mold charges. Low mass setters exhibit excellent thermal shock
properties and by reducing the mass of the overall furnace load. This enables rapid furnace
turnaround for firing parts that can withstand rapid cooling rates.
Item
FS-88
FS-90
Big Size
Volume density (g/cm3)
2.98
3.0
2.95
Show porosity (%)
20
15
18
Using Temperature
1650
1650
1650
Al2O3(%)
88
90.35
88.5
SiO2(%)
11.5
9.2
11.2
Fe2O3(%)
0.08
0.06
0.08
Applications
Magnetic materials, MIM powder metallurgy, etc