Flexane® Fast Cure Rubber Repair Liquid
Description:
A fast-curing, trowelable liquid urethane for repairing rubber equipment and filling expansion joints.
Intended Use:
Repair worn or damaged rubber equipment; form protective linings in equipment subject to wear, impact, abrasion,
vibration, expansion, and contraction.
Product
features:
400 ml reusable cartridge
Tack-free in 30 minutes
Fast, easy, no-mess dispensing
Thorough mixing of two components with automatic mix nozzle
Limitations:
Typical
Physical
Properties:
Technical data should be considered representative or typical only and should not be used for specification purposes.
Abrasion Resistance
Color
Coverage/lb
Cured Hardness
Cured Shrinkage
Dielectric Strength
Functional Cure
Maximum Elongation
Maximum Operating Temperature
Mix Ratio
Mixed Viscosity
Percent Solids by Volume
Pot Life
Specific Volume
Tear Resistance
Tensile Strength
Surface
Preparation:
TESTS CONDUCTED
Cured 7 days @ 75° F
Cure Shrinkage ASTM D 2566
330 mg loss per 1,000 revolutions (H
Dielectric Strength, volts/mil ASTM D 149
Grey
Tear Resistance ASTM D 624
106 sq.in./lb. @ 1/4"
Cured Hardness Shore D ASTM D 2240
94A
Tensile Strength (Urethanes) ASTM D 412
0.0018 in./in.
Maximum Elongation ASTM D 412
350 volts/mils
2 hrs.
450%
Dry: 180° Wet: 120°
F;
F
80 resin:20 curing agent /wt.
5,800 cps
100
8 min. @ 75°
F
26.5 in.(3) /lb.
430 pli
3,300 psi
For METAL SURFACES, thoroughly clean area to be repaired, rebuilt, or lined with Devcon® Cleaner Blend 300. Remove
any oil, grease, or dirt. Roughen surface by grinding with a coarse wheel or an abrasive disc pad. To prime this surface,
apply a coat of Devcon FL-10 Primer and allow to dry tack-free for 15 minutes. If the metal surface requires maximum tear
resistance or is exposed to moisture, or if submerged in water, use Devcon® FL-10 and Devcon® FL-20 Primer.
For RUBBER SURFACES, thoroughly clean area with an abrasive pad and Devcon® Cleaner Blend 300. Surface can also
be roughened with a grinding wheel so that it is coarse and free from oil and dirt that may clog the "pores" of the rubber.
Wipe or roughen surface with Cleaner Blend 300 until the cloth no longer picks up the color of the rubber. The rubber
should appear new or deeper in color. To prime this surface, apply a coat of Devcon® FL-20 Primer and allow to dry tackfree for 15-20 minutes. Use Devcon®FL-40 Primer on "hard-to-bond" rubber surfaces as this gives ultimate peel
resistance. Multiple coats may be necessary for porous rubber surfaces.
For MAXIMUM ADHESION, sandblast the surface with an angular abrasive until a minimum depth profile of 2-3 mils is
met. Blast to near-white finish specification SSPC-SP5 (Steel Structure Painting Council). Prime surface immediately after
sandblasting to prevent oxidation.
Mixing
Instructions:
---- To ensure proper cure speeds and hardness, mix Flexane at a temperature between 65°
F-85° ---F.
FOR 1 LB. UNITS
1.Add hardener to resin.
2.Vigorously mix with screwdriver or spatula for two minutes, while continuously scraping material away from sides and
bottom of container.
3.Transfer the mixed material to the plastic container (included in kit).
4.Wipe spatula clean, and stir again for two more minutes.