Brushable Ceramic White0 pages

Technical Data Sheet
1/26/2012

Brushable Ceramic White
Description:

A brushable, high-performance, ceramic-filled epoxy for sealing, protecting, and repairing surfaces subject to erosion,
corrosion, and wear

Intended Use:

Protect pump casings, impeller blades, gate valves, water boxes, and fan blades; rebuild heat exchangers, tube sheets,
and other water circulating equipment; top coat on repaired surfaces; seal and protect new equipment exposed to erosion
and corrosion

Product
features:

Excellent chemical resistance
Temperature resistance to 350°
F
Applies easily with short-bristle brush or roller
Low viscosity, self-leveling liquid
Acceptable for use in meat and poultry plants
NSF® Approved (Certified to ANSI/NSF61)

Limitations:

None

Typical
Physical
Properties:

Technical data should be considered representative or typical only and should not be used for specification purposes.
Adhesive Tensile Shear
Brush Coat Thickness
Coefficient of Thermal Expansion
Color
Compresive Strength
Coverage/lb
Cured Hardness
Cured Shrinkage
Dielectric Constant
Flexural Strength
Functional Cure
Mix Ratio by Volume
Mix Ratio by Weight
Mixed Viscosity
Pot Life @ 75F
Recoat Time
Salt Spray Resistance
Solids by Volume
Specific Gravity
Specific Volume
Temperature Resistance

Surface
Preparation:

TESTS CONDUCTED

Cured 7 days @ 75° F

Coef. of Thermal Expansion ASTM D 696
2,000 psi
Cure Shrinkage ASTM D 2566
10-20 mils (.010 - .020 in.)
Dielectric Strength, volts/mil ASTM D 149
19 [(in.) x (in). x ° x 10(-6)
F)]
Modulus of Elasticity ASTM D 638
White
Cured Hardness Shore D ASTM D 2240
15,200 psi
Adhesive Tensile Shear ASTM D 1002
7.6 sq.ft./lb. @ 15 mils(.015 in.)Compressive Strength ASTM D 695
Dielectric Constant ASTM D 150
87D
Flexural Strength ASTM D 790
0.0020 in./in.
Thermal Conductivity ASTM C 177
38.7
8,000 psi
16 hrs.
5.6:1
8.5:1
40,000 cps
21 min.
4-6 hrs.
5,000 hrs.
100
1.53 gm/cc
16.5 in.(3)/lb.
Wet 150°
F

1. Thoroughly clean the surface with Devcon® Cleaner Blend 300 to remove all oil, grease and dirt.
2. Grit blast surface area with 8-40 mesh grit, or grind with a coarse wheel or abrasive disc pad, to create increased
surface area for better adhesion (Caution: An abrasive disc pad can only be used provided white metal is revealed).
Desired profile is 3-5mil, including defined edges (do not "feather-edge” epoxy).
Note: For metals exposed to sea water or other salt solution, grit-blast and high-pressure-water-blast the area, then leave
overnight to allow any salts in the metal to “sweat” to the surface. Repeat blasting to “sweat out” all soluble salts. Perform
chloride contamination test to determine soluble salt content (should be no more than 40ppm).
3. Clean surface again with Devcon® Cleaner Blend 300 to remove all traces of oil, grease, dust or other foreign
substances from the grit blasting.
4. Repair surface as soon as possible to eliminate any changes or surface contaminants.

ITW Polymers Adhesives North America , 30 Endicott Street, Danvers, MA 01923

Tel:(978) 777-1100 www.itwadhesives.com