Ceramic Repair Putty
Description:
A high performance, trowelable, ceramic-filled epoxy for rebuilding worn or damaged equipment.
Intended Use:
Rebuild worn pump casings and suction plates; repair tube sheets, heat exchangers and other circulating water
equipment; restore worn chutes and hoppers; repair and rebuild butterfly and gate valves.
Product
features:
Excellent chemical resistance
Corrosion-, cavitation-, erosion-resistant
Non-sagging putty, creamy paste
Limitations:
None
Typical
Physical
Properties:
Technical data should be considered representative or typical only and should not be used for specification purposes.
Cured 7 days @ 75° F
Adhesive Tensile Shear
Coefficient of Thermal Expansion
Color
Compresive Strength
Coverage/lb
Cured Hardness
Cured Shrinkage
Dielectric Constant
Dielectric Strength
Flexural Strength
Functional Cure
Mix Ratio by Volume
Mix Ratio by Weight
Mixed Viscosity
Modulus of Elasticity
Pot Life @ 75F
Recoat Time
Solids by Volume
Specific Gravity
Specific Volume
Temperature Resistance
Thermal Conductivity
Surface
Preparation:
TESTS CONDUCTED
Adhesive Tensile Shear ASTM D 1002
Cure Shrinkage ASTM D 2566
Dielectric Strength, volts/mil ASTM D 149
Dielectric Constant ASTM D 150
Modulus of Elasticity ASTM D 638
Compressive Strength ASTM D 695
Cured Hardness Shore D ASTM D 2240
Coef. of Thermal Expansion ASTM D 696
Flexural Strength ASTM D 790
Thermal Conductivity ASTM C 177
2,000psi
17 [(in.)(in). x ° x 10(-6)
F)]
Dark Blue
12,700psi
66 sq.in./lb.@1/4"
90D
0.0022 in./in.
41.0
370 volts/mil
6,475 psi
16 hrs.
4.3:1
7:1
Putty
9.0 psi x 10(5)
25 minutes
2-4 hrs.
100
1.69 gm/cc
16.4 in.(3)/lb.
Wet 150° Dry 350°
F;
F
1.88 [(cal)/(sec x cm x °
C)]x10(-3)
1. Thoroughly clean the surface with Devcon® Cleaner Blend 300 to remove all oil, grease and dirt.
2. Grit blast surface area with 8-40 mesh grit, or grind with a coarse wheel or abrasive disc pad, to create increased
surface area for better adhesion (Caution: An abrasive disc pad can only be used provided white metal is revealed).
Desired profile is 3-5mil, including defined edges (do not "feather-edge” epoxy).
Note: For metals exposed to sea water or other salt solution, grit-blast and high-pressure-water-blast the area, then leave
overnight to allow any salts in the metal to “sweat” to the surface. Repeat blasting to “sweat out” all soluble salts. Perform
chloride contamination test to determine soluble salt content (should be no more than 40ppm).
3. Clean surface again with Devcon® Cleaner Blend 300 to remove all traces of oil, grease, dust or other foreign
substances from the grit blasting.
4. Repair surface as soon as possible to eliminate any changes or surface contaminants.
WORKING CONDITIONS: Ideal application temperature is 55° to 90° In cold working conditions, directly heat repair
F
F.
area to100-110° prior to applying epoxy and maintain at this temperature during product cure to dry off any moisture,
F
contamination or solvents, as well as to achieve maximum performance properties.